Evolution of ferronickel particles during the reduction of low-grade saprolitic laterite nickel ore by coal in the temperature range of 900–1250℃with the addition of CaO–CaF2–H3BO3

The method of producing ferronickel at low temperature(1250–1400℃)has been applied since the 1950s at Nippon Yakin Kogyo,Oheyama Works,Japan.Limestone was used as an additive to adjust the slag composition for lowering the slag melting point.The ferronickel product was recovered by means of a magnetic separator from semi-molten slag and metal after water quenching.To increase the efficiency of magnetic separation,a large particle size of ferronickel is desired.Therefore,in this study,the influences of CaO,CaF₂,and H₃BO₃ additives on the evolution of ferronickel particle at≤1250℃were investigated.The experiments were conducted at 900–1250℃with the addition of CaO,CaF₂,and H₃BO₃.The reduction processes were carried out in a horizontal tube furnace for 2 h under argon atmosphere.At 1250℃,with the CaO addition of 10 wt%of the ore weight,ferronickel particles with size of 20μm were obtained.The ferronickel particle size increased to 165μm by adding 10 wt%CaO and 10 wt%CaF₂.The addition of boric acid further increased the ferronickel particle size to 376μm,as shown by the experiments with the addition of 10 wt%CaO,10 wt%CaF₂,and 10 wt%H₃BO₃.     

粗大柱状晶纯镍热变形流变应力行为及加工图

采用Gleeble-3500热模拟机,在变形温度为950~1 150℃、应变速率为0.001~10s-1的条件下,研究了粗大柱状晶粒纯镍的热变形行为和加工图.结果表明:热压缩过程中流变应力随应变速率增大而增大,随变形温度降低而增大.流变应力与应变速率、变形温度之间的关系用Zener-Hollomon参数来描述,热变形激活能为312.4kJ/mol.基于动态材料模型(DMM)热加工图及结合合金相显微组织分析,得到纯镍较优的热加工参数:变形温度为1 060~1 120℃,应变速率为0.03~0.20s-1的蛋形区域.     

含镍废水的隔膜电解法回收工艺研究

以含有一定浓度硼酸的含镍电镀废水作为阴极液,2％的NaOH水溶液为阳极液,阴离子交换膜为隔膜材料组成隔膜电解装置,对含镍电镀废水进行了回收工艺研究。考察了电解时间、电流密度、pH值、温度及硼酸浓度对镍回收率的影响。结果表明,延长反应时间、提高电解温度、增加硼酸浓度有利于提高回收率。在电流密度为300 A／m2,pH=4,温度为35℃,硼酸浓度为25 g／L的最佳工艺条件下电解6 h,镍的回收率高达96.64％,所得镍为松枝状结构电解镍,纯度为94.69％。     

泵送减水剂对尾砂-棒磨砂膏体料浆和易性与充填体强度影响研究

针对金川镍矿尾砂-棒磨砂膏体在充填管道输送中存在的堵管问题,开展了泵送减水剂对膏体的和易性与充填体强度影响试验研究.首先分析了膏体物料的物化特性和颗粒级配;然后采用金川镍矿尾砂-棒磨砂膏体充填系统工业生产中的技术参数,开展了添加不同泵送减水剂添加量的充填体强度、膏体和易性以及流变特性参数测试研究.研究结果显示,当添加1%~2%的泵送减水剂,3、7和28 d强度均有显著提高.膏体的和易性随泵送减水剂添加量的增加而提高,且浓度越高,效果越显著.当膏体浓度(质量浓度)在78%~80%的范围,膏体初始剪切应力和粘滞系数均随着泵送减水剂的增加而线性减小.结合泵送减水剂对充填体强度、膏体和易性以及流变特性影响分析,并考虑膏体充填成本与采矿经济效益,确定1%的泵送减水剂为比较合理的添加量.研究结果为金川镍矿膏体充填系统料浆制备提供重要依据,已经应用于金川矿山膏体充填的工业化生产.     

氢氧化镍纳米片的制备及其超级电容性能

以尿素和氯化镍为原料,采用水热法制备了泡沫镍载Ni(OH)2纳米片电极,利用扫描电镜(SEM)观测了纳米片的形貌,利用X-射线衍射(XRD)分析了纳米片的结构,通过循环伏安和恒流充放电测试了电极的超级电容性能.检测结果表明:所制备的Ni(OH)2纳米片先构成一种交错连接的线状结构,再以线的形式均匀而密集地覆盖在泡沫镍的骨架上.这种特殊结构使得该纳米片电极表现出良好的电容性能,在电流密度为10mA/cm2的情况下,其面积比电容为255mF/cm2.     

镀镍碳纳米管对Mo_2FeB_2基金属陶瓷组织与性能的影响

采用化学镀法对碳纳米管进行表面镀镍处理,再利用真空液相烧结法制备出以镀镍碳纳米管为增强体的Mo_2FeB_2基金属陶瓷复合材料,借助SEM、EDS、硬度计等研究了添加镀镍碳纳米管对Mo_2FeB_2基金属陶瓷微观组织及力学性能的影响。结果表明,添加适量镀镍碳纳米管可细化Mo_2FeB_2基金属陶瓷组织并控制其孔洞尺寸及数量,显著提高其硬度及断裂韧性。当镀镍碳纳米管添加量为0.5%时,所得试样的晶粒最为细小,晶粒尺寸大约为1.2μm,材料的力学性能最佳,其硬度和断裂韧性分别达到1228.4HV0.3及15.90MPa·m12,相应增韧机制为裂纹偏转、桥接增韧、撕裂棱增韧和微孔洞增韧。     

利用PCR-DGGE技术分析硫化镍矿浸矿体系中的细菌群落演替

 浸矿体系中的菌群结构及其演替规律与浸出率具有密切的关系,为了解硫化镍矿浸矿体系中的这种关系以提高浸出率,利用PCR-DGGE(变性梯度凝胶电泳)技术结合16S rRNA基因序列对体系的细菌种群结构进行分析.研究表明,在硫化镍矿浸矿体系中,菌群组成菌属为嗜酸氧化亚铁硫杆菌属(Acidithiobacillus),并在浸矿体系中具有明显的演替现象,浸矿体系中的菌株演替和浸出率具有明显的相关性,经过21d的浸出,硫化镍矿的浸出率达到70%,探索浸矿体系中细菌的种群结构及其演替与浸出率的关系,对优化浸出体系菌群组成,提高浸出率具有指导作用.     

聚苯乙烯-甲基丙烯酸甲酯交联微球的制备及表面化学镀镍磁性化处理

采用苯乙烯（St）、甲基丙烯酸甲酯（MMA）、偶氮二异丁腈（AIBN）为引发剂,聚乙烯基吡咯烷酮（PVP-K30）为分散剂,无水乙醇和去离子水混合溶液为分散介质,三羟甲基丙烷三甲基丙烯酸酯（TMPTMA）为交联剂,以饥饿态加料方式加入第2种单体,用单分散聚合法制备了粒径分布窄、平均粒径为3～4μm的聚苯乙烯-甲基丙烯酸...     

热处理对镍基合金涂层与基体结合界面的影响

通过热浸镀法在普碳钢表面成功制备镍基合金涂层.为了提高镍基合金涂层与钢基体之间的结合强度,对镀有镍基合金涂层的基体进行了热处理.研究了热处理前、后结合界面处的显微组织和力学性能.结果表明,与热处理前相比,热处理后界面附近的涂层中析出物长大,界面处存在不连续块状铁的硼化物,界面两侧镍、铁互扩散距离增加,靠近界面的过渡带由5～8μm变为20μm.热处理前、后涂层均由γ-(Fe,Ni)、CrB、Cr2B和Cr3C2等相组成,过渡带相组成为γ-(Fe,Ni)、微量CrB和Fe23(C,B)6.热处理后,显微硬度由界面向涂层内逐渐增加,界面结合强度由140MPa提高到200MPa.     

Cl~-对690合金腐蚀电化学行为的影响

采用动电位极化、电化学阻抗、动电位电化学阻抗谱和电容测量等方法研究了690合金在一回路模拟溶液中的电化学行为.极化曲线结果表明:690合金在两种溶液中都存在较窄的钝化区间,在0.5V出现二次钝化现象.电化学阻抗表明,690合金在不含Cl-溶液中的阻抗模值较大,而随Cl-的加入阻抗模值变小.动电位电化学阻抗谱表明,随扫描电位正移,钝化膜在两种溶液中具有相似的变化趋势,动电位电化学阻抗谱与动电位极化曲线完全对应.690合金在0.2V下形成的钝化膜的Mott-Schottky曲线测量表明,溶液中Cl-使得钝化膜中的施主和受主密度增大.